Dynamics Flex Film 200

Product Description: Flex Film 200 is a heat-stabilized co-extruded film modified from a modified PA resin it is a high temperature bagging film which can be used for cures up to 205°C / 401°F. Recommended for advanced composite fabrication and other high-temperature/pressure application where softness workability pinhole-free and defect-free film are essential. TECHNICAL PROPERTIES MAX Working Temperature: 205°C – 401°F APPLICATION SYSTEM Polyester Vinyl Ester and Epoxy Resins TENSILE STRENGTH ASTM D882 MD 60MPa TENSILE STRENGTH ASTM D882 TD 60MPa ELONGATION AT BREAK (ASTM D882) MD 270% ELONGATION AT BREAK (ASTM D882) TD 280% STANDARD THICKNESS 0055mm – 0075mm 0.0020in – 0.003in PLANAR DENSITY 0063 / 0085 KgM2 ORDER UNITY Square Meters M2 STANDARD WIDTHS 1520mm – 3040mm – 4060mm / 60in 120in 160in AVAILABLE FORMATS Sheet Tube V-Sheet NOTES Suitable for autoclave cure process. All PA-based films absorb water. The water or moisture absorption will soften the film and a high content of moisture is the perfect condition for flexibility performance. Flex Film is packed in roll and in polyethylene bag and must be stored in a clean and humid environment with 50%-70% RH and 10°C-25°C temperature.